Gray lron |
Standard-Spec.No.&Class标准 | T.S. σb≥ N/mm2 | Hardness HB≤ | Note:(1)Test Bar θ=30mm(2)Chemieal composition and other requirement can be established upon written agreement between manufacturer and purchaser.(3)The hardness values are for castings of 15~30mm thickness. | ||
GB China/ISO | JIS JAPAN | ASTM U.S.A. | |||
HT200/200 | FC200 | CI.30 | 200 | 223 | |
HT250-250 | FC250 | CI.35 | 250 | 241 | |
HT300/300 | FC300 | CI.40 | 300 | 262 | |
HT350/350 | FC350 | CI.50 | 350 | 277 |
Ductile lron |
Standard-Spec.No&Class | T.S. σb≥ N/mm2 | Y.S. σs ≥% | EL σ≥ | For Reference | Note: | |||
GB China | JIS Japan | ASTM A536 U.S.A. | Hardness HB | Micor-structure | ||||
QT400-18 | FCD400-18 | 60-40-18 | 400 | 250 | 18 | 130-180 | Ferrite(F) | |
QT450-10 | FCD450-10 | 450 | 310 | 10 | 160-210 | (F) | ||
QT500-7 | FCD500-7 | 65-45-12 | 500 | 320 | 7 | 170-230 | (F)+Pearlite(P) | |
QT600-3 | FCD600-3 | 80-55-06 | 600 | 370 | 3 | 190-270 | (P)+(F) | |
QT700-2 | FCD700-2 | 100-70-03 | 700 | 480 | 2 | 225-305 | (P) | |
QT800-2 | FCD800-2 | 100-70-03 | 800 | 480 | 3 | 245-335 | (P)or tempered structure |
Alloy Cast lron for Special Use |
Standard-Spec.No. | Chemical Composition% | Mechanical properties | Micro-Structure (as cast) | |||||||
GB China | JIS Japan | ASTM U.S.A. | C | Mn | Si | Cr | Others | T.S. σb N/mm2 | Hardness | |
Heat-Resistant Ductile lron (Heat-Resistant Temp.750-900℃) | ||||||||||
RQTSI-5 | 2.4-3.2 | ≤0.7 | 4.5-5.5 | Mg0.035-0.065 RE0.015-0.04 | ≥370 | HB 228-302 | (F) | |||
Wear-Resistant Cast lron | ||||||||||
KmTBCr15Mo2-GT | A532IIC | 2.8-3.5 | 0.5-1.0 | ≤1.0 | 13.0-18.0 | Mo0.5-3.0,Ni0-1.0 Cu0-1.2 | HRC50-58 | (M,A) | ||
KmTBCr26 | A532IIIA | 2.3-3.0 | 0.5-1.0 | ≤1.0 | 23.0-28.0 | Mo 0-1.0,Ni 0-1.5 Cu 0-2.0 | HRC50-58 | (M) | ||
Corrosion-Resistant Cast lron | ||||||||||
STSi15 R | ≤1.0 | ≤0.5 | 14.25-15.75 | RE<0.1 | HRC≤48 | (F) |
Plain Carbon Cast Steel |
Standard-Spec.No.& Grade | Chemical Composition≤% | Mechanical Properties≥ | NOTE:(1)S,P≤0.04%(2)C,Mn%can also be agreed upon by manufacturer and purchaser.(3)Heat Treat:Normalize(N)+Temper(T) or Quench(Q)+T,selected by Foundry | |||||||
GB China | JIS Japan | ASTM U.S.A. | C | Si | Mn | T.S. σb N/mm2 | Y.S. σs N/mm2 | EL σ% | R.A. ψ% | |
ZG200-400 | SC420 | A27 60-30 | 0.2 | 0.5 | 0.8 | 400 | 200 | 25 | 40 | |
ZG230-450 | SC450 | 65-35 | 0.3 | 0.9 | 450 | 230 | 22 | 32 | ||
ZG270-500 | SC480 | 70-40 | 0.4 | 500 | 270 | 18 | 25 | |||
ZG340-640 | SCC3B | A148 80-50 | 0.6 | 0.6 | 640 | 240 | 10 | 18 |
Low Alloy Cast Steel低合金铸钢 |
Standard-Spec.No.标准 | Chemical Composition% | Heat Treat [热处理] | Mechanical Properties≥ | ||||||||||
GB China | JIS Japan | AISi U.S.A | C | Si | Mn | Cr | Mo | T.S. σb N/mm2 | Y.S. σs N/mm2 | EL σ% | R.A. ψ% | Hardness | |
ZG40Mn2 | SMn443 | 1340 | 0.35-0.45 | 0.20-0.40 | 1.60-1.80 | Q+T | 830 | 650 | 13 | 45 | 269-302 | ||
ZG40Cr | SCr440 | 5140 | 0.35-0.45 | 0.20-0.40 | 0.50-0.80 | 0.80-1.10 | N+T | 570 | 345 | 18 | 26 | ≤212 | |
ZG35CrMnSi | SCMnCr3 | 0.30-0.40 | 0.50-0.75 | 0.60-1.20 | 0.50-0.80 | N+T | 570 | 345 | 14 | 30 | ≤217 | ||
ZG35CrMo | SCCrM3 | 4135 | 0.30-0.40 | 0.20-0.40 | 0.50-0.80 | 0.80-1.10 | 0.20-0.30 | Q+T | 700 | 535 | 12 | 25 | ≤200 |
High Alloy Cast Steel高合金铸钢 |
Standard-Spec.No标准 | Chemical Composition% | Mechanical Properties≥ | |||||||||
GB China | JIS Japan | ASTM (AISI) U.S.A. | C | Si | Mn | Cr | Ni | Others (其它) | T.S. σb N/mm2 | Y.S. | EL σ% |
ZG1Cr13 | SCSI | CA-15(410) | ≤0.15 | ≤1.50 | ≤1.00 | 11.5-14.0 | ≤1.00 | Mo≤0.05 | 620 | 450 | 16 |
ZG0Cr18Ni9 | SCS13 | CF8(304) | ≤0.08 | ≤2.00 | ≤1.50 | 18.0-21.0 | 8.0-11.0 | 440 | 185 | 30 | |
ZG1Cr18Ni9 | SCS12 | CF20(302) | ≤0.20 | ≤2.00 | ≤1.50 | 18.0-21.0 | 8.0-11.0 | 480 | 205 | 28 | |
ZG0Cr18Ni12Mo2Ti | SUS316 | CF-8M(316) | ≤0.08 | ≤1.50 | ≤1.50 | 18.0-21.0 | 9.0-12.0 | Mo 2.0-3.0 Ti0.7 | 490 | 216 | 30 |
ZG0Cr17Ni4Cu4Nb | SUS630 | CB-7Cu 17-4PH | ≤0.07 | ≤1.00 | ≤1.00 | 15.5-17.0 | 3.0-5.0 | Cu2.3-3.0 Nb0.14-0.45 | 980 | 785 | 5 |
ZGMN13-3 | SCMnH2 | A128 B-1 | 0.90-1.30 | 0.30-0.80 | 11.0-14.0 | S≤0.05, P≤0.08 | 686 | 35 | |||
ZG3Cr18Ni25Si2 | SCH19 | A297 HN | 0.20-0.50 | ≤2.00 | ≤2.00 | 19.0-23.0 | 23.0-27.0 | Mo≤0.50 | 435 | 230 | 8 |
ZG4Cr25Ni20Si2 | SCH22 | A351 HK-40 | 0.35-0.45 | ≤1.75 | ≤1.50 | 23.0-27.0 | 19.0-22.0 | 450 | 240 | 10 |
Aluminum-base Cast Alloy铸造铝合金 |
Standard-Spec.No.标准 | Chemical Composition% | Process (工艺) | Condi tion ( 状态) | Mechanical Properties≥ | ||||||||||||
GB China | Code China | JIS Japan | Alcoa (ASTM) | Si | Cu | Mg | Mn | Ti | Ni | Ai | T.S. σb N/mm2 | Hardness HB | EL σ% | |||
ZAISi7Mg | ZL 101 | AC4C | 356 (SG70A) | 6.5-7.5 | 0.25-0.45 | Ba lance (余量) | S;J SB | F T6 | 155 220 | 50 70 | 2 1 | |||||
ZAISi9Mg | ZL 104 | AC4A | 360 | 8.0-10.5 | 0.17-0.30 | 0.2-0.5 | SB | T6 | 220 | 70 | 2 | |||||
ZAISi5Cu1 | ZL 105 | AC4D | 355 (SC51A) | 4.5-5.5 | 1.0-1.5 | 0.4-0.6 | S | T6 | 220 | 70 | 0。5 | |||||
ZAISi12Cu | ZL 109 | AC8A | A132 | 11.0-13.0 | 0.5-1.5 | 0.8-1.3 | 0.8-1.5 | T6 | 240 | 100 | ||||||
i1 | ||||||||||||||||
ZAICu5Mu | ZL 201 | 4.5-5.3 | 0.60-1.0 | 0.15-0.35 | S;J | T5 | 330 | 90 | 4 | |||||||
ZAIMg5Si1 | ZL 303 | 0.8-1.3 | 4.5-5.5 | 0.1-0.4 | S;J | F | 145 | 55 | 1 |
Copper-base Cast Alloy铸造铜合金 |
Standard-Spec.No.标准 | Chemical Composition% | Mechanical Properties≥ | Process (工艺) | |||||||||||||
GB China | JIS Japan | ASTM U.S.A | Sn | Zn | Pb | Si | Cu | T.S. σb N/mm2 | Y.S. σ% | EL HBW | Hardness | |||||
ZCuSn5Pb5Zn5 | BC6 | C83600 | 4.0-6.0 | 4.0-6.0 | 4.0-6.0 | Balance (余量) | 200 | 90 | 13 | 60 | S;J | |||||
ZCuSn10Zn2 | BC3 | C90500 | 9.0-11.0 | 1.0-3.0 | 240 | 120 | 12 | 70 | S | |||||||
ZCuZn16Si4 | SZBC3 | C87800 | Balance (余量) | 2.5-4.5 | 79.5-81.0 | 390 | 20 | 100 | J | |||||||
ZCuZn40Pb2 | C85700 | 0.5-2.5 | 58.0-63.0 | 220 | 120 | 15 | 80 | S |